Fine filler with high elasticity for sealing pores and for repairing small scratches, grooves and uneven surfaces

Finely matched filler and resin combinations

Non-porous and closed filling
Low dust build-up during sanding

Quick drying

Saves time as further processing can continue directly (sanding, filling and applying top coat)

Easy to sand

User friendly
Simplifies further processing of the object

Brilliant white pigmentation

Optimum surface and preparation for top-coat paint
Ideal for use in model and furniture construction

Temperature-resistant up to 80u00b0C

Notice

Tip: Before the final coating, skim the repaired spot with 1-component or 2-component universal primer, HS filler or Rust Stop Quattro (to eliminate the risk of visible repair edges or gloss reduction)

Maximum permissible VOC content of VAKU 20: 250 g/l of product category 2(b). Max. VOC content in accordance with German Ordinance on Solvent-Based Paints and Lacquers (ChemVOC FarbV): 2 g/l

The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.

Application

Automotive/cargo

For eliminating minor paint damage, scratches and for closing pores and uneven areas in filling and universal filling applications.

Metal

Extremely fine surface processing to ensure an optimum finish.

Wood

Suitable as a fine filler or universal filler for all types of wood. Not suitable for oily types of wood. Do not use on heavily weathered surfaces.

Instructions

The surface must be clean, dry and free from grease

Sand surfaces

Due to water sensitivity, polyester material should only be sanded when dry where possible

To prevent possible complaints, always ensure the correct dosing ratio of filler to hardener is used

Dosing: 2% hardener

Pot life

4-5 minutes at 20u00b0C

Drying time

20-30 minutes at 20u00b0C

Sandpaper

P80-280
Wet sand only once completely dry

Technical information

Smell/fragrance	Characteristic
Weight of content	970 g
Conditions for VOC concentration	ChemVOCFarb
Chemical basis	Polyester resin
Colour	White
Hardener content	2 %
Density	1.109 g/cmu00b3
Density conditions	at 20u00b0C
Max. working life	5 min
Min. working life	4 min
Conditions for working life	at 20u00b0C
Conditions for drying time	at 20u00b0C
Min. drying time	20 min
Max. drying time	30 min
Max. temperature resistance of the hardened material	80 u00b0C
Max. permissible VOC concentration	250 g/l
Max. VOC concentration	2 g/l
Shelf life from production	12 Month
Additional articles	Sandpaper Useit, art. no. 058130..., 058131..., 0581330...

Additional accessory:

Art.-no.: 0892600004

Hardener for filler

HDNR-FILR-VAKU-TUBE-40G

Suitable glove:

Natural latex and neoprene chemical protective glove

Permeation level: 1

Cotton flocking on the inside

Butyl chemical protective glove

Permeation level: 3

Gas-tight and resistant to exhaust gases produced by combustion processes

Permeation is the process by which a chemical moves through the material of a protective glove on a molecular level. The time from the initial contact between the chemical and the glove to the permeation of the material is the breakthrough time.

Measured breakthrough time	Permeation level
< 10 min	0
u2265 10 min	1
u2265 30 min	2
u2265 60 min	3
u2265 120 min	4
u2265 240 min	5
u2265 480 min	6

Important information:

The information given is based on experience and laboratory conditions and is designed as a guide. However, the actual suitability of a glove depends on the individual conditions of its use and must be confirmed by an appropriate test under operational conditions. Given the variety of materials and chemicals used, the possibility of incompatibility or usage problems for the wearer cannot be excluded in individual cases. We would be happy to advise you about optimum solutions.

Product information