Technical chemicals Adhesives Structural adhesives Structural adhesive
Structural adhesive Bond + Seal Fast
Structural adhesive Bond + Seal Fast
+374(0)10 349347, 349348
Tecnical Description
- Silicone-free: Yes
- Smell/fragrance: Characteristic
- Container: Cartridge
- Contents: 300 ml
- Min./max. temperature resistance: -40 to 90 °C
- Chemical basis: Single component polyurethane
- Max. short-term temperature resistance: 120 °C
- Min./max. processing temperature: 5 to 35 °C
- Min. flashing point: 65 °C
- Conditions for tensile strength: in accordance with DIN 53504
- Full curing speed/conditions: 3 mm/d / 23°C and 50% relative humidity, moisture curing
- Fully hardening/curing conditions: 23°C and 50% relative humidity, moisture curing
- Shore A hardness: 40
- Min. tensile strength: 1.8 N/mm²
- Min. longitudinal resistance to tearing: 6 N/mm
- Conditions for resistance to tearing: in accordance with DIN 53515
- Glass transition temperature/conditions: -45 °C / in accordance with DIN 53445
- Shelf life from production/conditions: 12 Month / at 10°C to 25°C
- Short-term resistance against: Fuels, Mineral oils, Animal fat, Animal oils, Vegetable fat, Vegetable oils
- Min./max. skin-formation time: 19-20 min
- Elongation at break: 600 %
- Elongation at break/conditions: 600 % / in accordance with DIN 53504
- Max. volume change/conditions: -6 % / in accordance with DIN 52451
- Resistance against: Water, Lime water, Public sewage, Diluted inorganic acids and lyes, Salt water
Density/condi...
Ultraviolet resistance
Chemical basis
Code
Package / Quantity
Price (AMD)
1,2 g/cm³ / at 23°C, 50% relative humidity
Yes
Single component polyurethane
Code: 0890100720
Tecnical Description
- Colour Grey
- Density/condi... 1,2 g/cm³ / at 23°C, 50% relative humidity
- Ultraviolet resistance Yes
- Chemical basis Single component polyurethane
- Smell/fragrance Characteristic
- Min./max. skin-formation time 19-20 min
- Full curing speed/conditions 3 mm/d / 23°C and 50% relative humidity, moisture curing
- Fully hardening/curing conditions 23°C and 50% relative humidity, moisture curing
- Shore A hardness 40
- Min. tensile strength 1.8 N/mm²
- Conditions for tensile strength in accordance with DIN 53504
- Min. longitudinal resistance to tearing 6 N/mm
- Conditions for resistance to tearing in accordance with DIN 53515
- Elongation at break 600 %
- Elongation at break/conditions 600 % / in accordance with DIN 53504
- Min./max. processing temperature 5 to 35 °C
- Min./max. temperature resistance -40 to 90 °C
- Max. short-term temperature resistance 120 °C
- Min. flashing point 65 °C
- Glass transition temperature/conditions -45 °C / in accordance with DIN 53445
- Max. volume change/conditions -6 % / in accordance with DIN 52451
- Shelf life from production/conditions 12 Month / at 10°C to 25°C
- Silicone-free Yes
- Resistance against Water, Lime water, Public sewage, Diluted inorganic acids and lyes, Salt water
- Short-term resistance against Fuels, Mineral oils, Animal fat, Animal oils, Vegetable fat, Vegetable oils
- Contents 300 ml
- Container Cartridge
1,2 g/cm³ / at 23°C, 50% relative humidity
Yes
Single component polyurethane
Code: 0890100730
Tecnical Description
- Shelf life from production/conditions 12 Month / at 10°C to 25°C
- Max. volume change/conditions -6 % / in accordance with DIN 52451
- Chemical basis Single component polyurethane
- Short-term resistance against Fuels, Mineral oils, Animal fat, Animal oils, Vegetable fat, Vegetable oils
- Min./max. temperature resistance -40 to 90 °C
- Density/condi... 1,2 g/cm³ / at 23°C, 50% relative humidity
- Container Cartridge
- Elongation at break/conditions 600 % / in accordance with DIN 53504
- Min. flashing point 65 °C
- Glass transition temperature/conditions -45 °C / in accordance with DIN 53445
- Conditions for resistance to tearing in accordance with DIN 53515
- Ultraviolet resistance Yes
- Max. short-term temperature resistance 120 °C
- Conditions for tensile strength in accordance with DIN 53504
- Elongation at break 600 %
- Smell/fragrance Characteristic
- Shore A hardness 40
- Min. longitudinal resistance to tearing 6 N/mm
- Full curing speed/conditions 3 mm/d / 23°C and 50% relative humidity, moisture curing
- Min./max. skin-formation time 19-20 min
- Fully hardening/curing conditions 23°C and 50% relative humidity, moisture curing
- Min. tensile strength 1.8 N/mm²
- Silicone-free Yes
- Contents 300 ml
- Resistance against Water, Lime water, Public sewage, Diluted inorganic acids and lyes, Salt water
- Min./max. processing temperature 5 to 35 °C
Code: 0890100710
Product information
Catalogue page as PDF 1
Tecnical Description
- Elongation at break 600 %
- Ultraviolet resistance No
- Chemical basis Single component polyurethane
- Contents 300 ml
- Max. short-term temperature resistance 120 °C
- Min. tensile strength 1.8 N/mm²
- Smell/fragrance Characteristic
- Min./max. skin-formation time 19-20 min
- Density/condi... 1,27 g/cm³ / at 20°C
- Resistance against Water, Lime water, Public sewage, Diluted inorganic acids and lyes, Salt water
- Container Cartridge
- Full curing speed/conditions 3 mm/d / 23°C and 50% relative humidity, moisture curing
- Shore A hardness 40
- Fully hardening/curing conditions 23°C and 50% relative humidity, moisture curing
- Min. longitudinal resistance to tearing 6 N/mm
- Conditions for resistance to tearing in accordance with DIN 53515
- Max. volume change/conditions -6 % / in accordance with DIN 52451
- Elongation at break/conditions 600 % / in accordance with DIN 53504
- Min./max. temperature resistance -40 to 90 °C
- Shelf life from production/conditions 12 Month / at 10°C to 25°C
- Glass transition temperature/conditions -45 °C / in accordance with DIN 53445
- Min./max. processing temperature 5 to 35 °C
- Short-term resistance against Fuels, Mineral oils, Animal fat, Animal oils, Vegetable fat, Vegetable oils
- Min. flashing point 65 °C
- Silicone-free Yes
- Conditions for tensile strength in accordance with DIN 53504
Highly adhesive, permanently elastic sealing compound
- Very good adhesion to plain, primed and painted sheet metal
- Compensates for tolerances/bridges gaps
- Long-term, reliable seals
High degree of stability
- Very easy to smooth
- Spatula and brush application
- Can be structured with brush or smoothing stick
Short skin formation time
The sealant surface is tack-free after a short period.
Can be painted over quickly
Thanks to the quick skin formation time (perform preliminary tests to check paint compatibility).
Approved for use with foodstuffs (ISEGA certificate)
- Harmless to health in hardened state
- Suitable for sealing in food processing areas
Non-corrosive
Prevents metal corrosion.
Virtually odourless
Silicone-free
Notice
Do not allow this product to come into contact with alkyd-resin paint systems. Not suitable for glass groove sealing in areas in which UV back reflection can occur. Direct exposure to sunlight can result in slight surface yellowing. It is essential to use Würth B and S Primer products in order to achieve optimum adhesion results! This is especially important with critical surfaces, such as non-ferrous base metals (copper) and galvanised materials. For smoothing, use Würth sealant smoothing agent.
The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.