Filler VAKU 50 089260501

0x - +	Գինը գրանցվելուց հետո	Ավելացնել զամբյուղ

Specification

Elastic contour filler, specifically for use on paintable plastic parts

High degree of elasticity

Ideal for modelling and touching up contours

Excellent adhesion

Short drying time

Saves time as further processing can continue directly

Easy to sand

User friendly

Can also be used on other material substrates

Multifunctional

Maximum permissible VOC content of VAKU 50: 250 g/l of product category 2(b). Max. VOC content in accordance with German Ordinance on Solvent-Based Paints and Lacquers (ChemVOC FarbV): 3 g/l.

Heat-resistant up to 80u00b0C

Notice

Tip: Preliminary tests are recommended due to the broad range of mixed plastics! Pre-treatment with a 1-component plastic primer is advisable to ensure optimum adhesion.

Not suitable for repairing breakage points.

To prevent possible complaints, always ensure the correct dosing ratio between the filler and hardener.

The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.

Application

Auto/cargo:

In vehicle manufacturing and for repairing vehicles. Elastic filler for repairing scratches, indents and contours (e.g. contact damage on bumpers) on paintable plastic parts.

Metal:

Elastic filler for repairing scratches, recesses and contours on paintable plastic parts.

Instructions

The surface must be clean, dry and free from grease. Sand surfaces Wherever possible, only sand polyester material when dry due to its sensitivity to water. See separate information on wet sanding.

Technical information

Contents	590 ml
Smell/fragrance	Characteristic
Weight of content	970 g
Conditions for VOC concentration	ChemVOCFarb
Chemical basis	Styrene
Colour	Anthracite
Hardener content	2 %
Density	1.858 g/cmu00b3
Max. working life	5 min
Min. working life	4 min
Conditions for working life	at 20u00b0C
Conditions for drying time	at 20u00b0C
Min. drying time	20 min
Max. drying time	30 min
Max. temperature resistance of the hardened material	80 u00b0C
Max. permissible VOC concentration	250 g/l
Max. VOC concentration	3 g/l
Shelf life from production	12 Month

Suitable glove:

Natural latex and neoprene chemical protective glove

Permeation level: 1

Cotton flocking on the inside

Butyl chemical protective glove

Permeation level: 3

Gas-tight and resistant to exhaust gases produced by combustion processes

Permeation is the process by which a chemical moves through the material of a protective glove on a molecular level. The time from the initial contact between the chemical and the glove to the permeation of the material is the breakthrough time.

Measured breakthrough time	Permeation level
< 10 min	0
u2265 10 min	1
u2265 30 min	2
u2265 60 min	3
u2265 120 min	4
u2265 240 min	5
u2265 480 min	6

Important information:

The information given is based on experience and laboratory conditions and is designed as a guide. However, the actual suitability of a glove depends on the individual conditions of its use and must be confirmed by an appropriate test under operational conditions. Given the variety of materials and chemicals used, the possibility of incompatibility or usage problems for the wearer cannot be excluded in individual cases. We would be happy to advise you about optimum solutions.